GooseGrl172 wrote:
Well it's unlikely that there would have been a sudden drop (as depicted in the movie) no matter the angle, since it is the bending and tearing of the metal that would have had the stern settle slowly back. Not necessarily the degree angle it was at (although a lower angle would have had more stress at the break point than a higher angle).

Jessica